Fused Deposition Modelling (FDM) provides opportunities for new development in numerous areas. Z-directional anisotropic strength caused by weak inter-layer bonding has been recognized as the reason for limited industry adoption of FDM. This paper aims to investigate increasing the Z-directional strength of Acrylonitrile Butadiene Styrene (ABS) using a temperature controlled print environment. The ambient temperature during printing was increased to reduce heat transfer from the print, thereby encouraging more polymer chain inter-diffusion between layers. Dogbone specimens were printed at ambient print temperatures between 24.8°C and 71.2°C and tensile tests were performed. A thermal camera was used to identify heat loss in the FDM process. Ultimate tensile strength was found to increase by a maximum of 104% compared to open enclosure printing. A stylus profiler and scanning electron microscopy were used to compare the quality of the inter-layer bonds, suggesting that additional polymer inter-diffusion occurred at hotter ambient temperatures. A weak positive relationship was found between ambient air temperature and inter-layer part strength. Further experimentation could provide scope to determine an ideal ambient print temperature that is likely to be dependent on print settings and the printer used.

This content is only available via PDF.
You do not currently have access to this content.