Research Papers

Material Influence on Mitigation of Stress Corrosion Cracking Via Laser Shock Peening

[+] Author and Article Information
Grant Brandal

Department of Mechanical Engineering,
Columbia University,
500 W 120th Street, Mudd Rm 220,
New York, NY 10027
e-mail: gbb2114@columbia.edu

Y. Lawrence Yao

Fellow ASME
Department of Mechanical Engineering,
Columbia University,
New York, NY 10027
e-mail: yly1@columbia.edu

1Corresponding author.

Contributed by the Manufacturing Engineering Division of ASME for publication in the JOURNAL OF MANUFACTURING SCIENCE AND ENGINEERING. Manuscript received March 4, 2016; final manuscript received July 5, 2016; published online August 8, 2016. Assoc. Editor: Hongqiang Chen.

J. Manuf. Sci. Eng 139(1), 011002 (Aug 08, 2016) (10 pages) Paper No: MANU-16-1141; doi: 10.1115/1.4034283 History: Received March 04, 2016; Revised July 05, 2016

Stress corrosion cracking is a phenomenon that can lead to sudden failure of metallic components. Here, we use laser shock peening (LSP) as a surface treatment for mitigation of stress corrosion cracking (SCC), and explore how the material differences of 304 stainless steel, 4140 high strength steel, and 260 brass affect their mitigation. Cathodic charging of the samples in 1 M sulfuric acid was performed to accelerate hydrogen uptake. Nontreated stainless steel samples underwent hardness increases of 28%, but LSP treated samples only increased in the range of 0–8%, indicative that LSP keeps hydrogen from permeating into the metal. Similarly for the high strength steel, LSP treating limited the hardness changes from hydrogen to less than 5%. Mechanical U-bends subjected to Mattsson's solution, NaCl, and MgCl2 environments are analyzed, to determine changes in fracture morphology. LSP treating increased the time to failure by 65% for the stainless steel, and by 40% for the high strength steel. LSP treating of the brass showed no improvement in U-bend tests. Surface chemical effects are addressed via Kelvin Probe Force Microscopy, and a finite element model comparing induced stresses is developed. Detection of any deformation induced martensite phases, which may be detrimental, is performed using X-ray diffraction. We find LSP to be beneficial for stainless and high strength steels but does not improve brass's SCC resistance. With our analysis methods, we provide a description accounting for differences between the materials, and subsequently highlight important processing considerations for implementation of the process.

Copyright © 2017 by ASME
Your Session has timed out. Please sign back in to continue.


Brandl, E. , Malke, R. , Beck, T. , Wanner, A. , and Hack, T. , 2009, “ Stress Corrosion Cracking and Selective Corrosion of Copper-Zinc Alloys for the Drinking Water Installation,” Mater. Corros., 60(4), pp. 251–258. [CrossRef]
Rice, S. , 2015, “ Epic Energy Finds Gas Pipeline Rupture Was Caused by Stress Corrosion Cracking,” The Advertiser, Adelaide, Australia, Apr. 22.
Cox, B. , 1990, “ Environmentally-Induced Cracking of Zirconium Alloys—A Review,” J. Nucl. Mater., 170(1), pp. 1–23. [CrossRef]
Obata, M. , Sudo, A. , and Matsumoto, J. , 1996, “ The Effect of Shot Peening on Residual Stress and Stress Corrosion Cracking for Austenitic Stainless Steel,” 6th International conference on Shot Peening, pp. 24–33.
Chen, H. , Yao, Y. L. , and Kysar, J. W. , 2004, “ Spatially Resolved Characterization of Residual Stress Induced by Micro Scale Laser Shock Peening,” ASME J. Manuf. Sci. Eng., 126(2), p. 226. [CrossRef]
Zhang, Y. , Lu, J. , and Luo, K. , 2013, “ Stress Corrosion Cracking Resistance of AISI 304 SS Subjected to Laser Shock Processing,” Laser Shock Processing of FCC Metals, Springer, Berlin, Germany, pp. 137–152.
Peyre, P. , Braham, C. , Ledion, J. , Berthe, L. , and Fabbro, R. , 2000, “ Corrosion Reactivity of Laser-Peened Steel Surfaces,” J. Mater. Eng. Perform., 9(6), pp. 656–662. [CrossRef]
Birnbaum, H. K. , and Sofronis, P. , 1994, “ Hydrogen-Enhanced Localized Plasticity—A Mechanism for Hydrogen-Related Fracture,” Mater. Sci. Eng. A, 176(1–2), pp. 191–202. [CrossRef]
Akid, R. , and Dmytrakh, I. , 1998, “ Influence of Surface Deformation and Electrochemical Variables on Corrosion and Corrosion Fatigue Crack Development,” Fatigue Fract. Eng. Mater. Struct., 21(7), pp. 903–911. [CrossRef]
Shewmon, P. , 1989, Diffusion in Solids, The Minerals, Metals, and Materials Society, Warrendale, PA.
Hirth, J. P. , 1980, “ Effects of Hydrogen on the Properties of Iron and Steel,” Metall. Trans. A, 11(6), pp. 861–890. [CrossRef]
Kamoutsi, H. , Haidemenopoulos, G. N. , Bontozoglou, V. , and Pantelakis, S. , 2006, “ Corrosion-Induced Hydrogen Embrittlement in Aluminum Alloy 2024,” Corros. Sci., 48(5), pp. 1209–1224. [CrossRef]
Peyre, P. , and Fabbro, R. , 1995, “ Laser Shock Processing: A Review of the Physics and Applications,” Opt. Quantum Electron., 27(12), pp. 1213–1229.
Fan, Y. , Wang, Y. , Vukelic, S. , and Yao, Y. L. , 2005, “ Wave-Solid Interactions in Laser-Shock-Induced Deformation Processes,” J. Appl. Phys., 98(10), p. 104904. [CrossRef]
Navai, F. , 1995, “ Effects of Tensile and Compressive Stresses on the Passive Layers Formed on a Type 302 Stainless Steel in a Normal Sulphuric Acid Bath,” J. Mater. Sci., 30(5), pp. 1166–1172. [CrossRef]
Chen, H. , Kysar, J. W. , and Yao, Y. L. , 2004, “ Characterization of Plastic Deformation Induced by Microscale Laser Shock Peening,” ASME J. Appl. Mech., 71(5), p. 713. [CrossRef]
Krom, A. H. M. , and Bakker, A. , 2000, “ Hydrogen Trapping Models in Steel,” Metall. Mater. Trans. B, 31(6), pp. 1475–1482. [CrossRef]
Malygin, G. A. , 1990, “ Dislocation Density Evolution Equation and Strain Hardening of F.C.C. Crystals,” Phys. Status Solidi, 119(2), pp. 423–436. [CrossRef]
Druffner, C. , Schumaker, E. , and Sathish, S. , 2004, “ Scanning Probe Microscopy,” Nondestructive Materials Characterization, N. G. H. Meyendorf , ed., Springer-Verlag, Berlin, Germany, pp. 323–355.
Schmutz, P. , and Frankel, G. S. , 1998, “ Characterization of AA2024-T3 by Scanning Kelvin Probe Force Microscopy,” J. Electrochem. Soc., 145(7), pp. 2285–2295. [CrossRef]
Stratmann, M. , and Streckel, H. , 1990, “ On the Atmospheric Corrosion of Metals Which are Covered With Thin Electrolyte Layers—I: Verification of the Experimental Technique,” Corros. Sci., 30(6–7), pp. 681–696. [CrossRef]
Wang, X. F. , Li, W. , Lin, J. G. , and Xiao, Y. , 2010, “ Electronic Work Function of the Cu (100) Surface Under Different Strain States,” Europhys. Lett., 89(6), p. 66004. [CrossRef]
Li, W. , and Li, D. Y. , 2005, “ Variations of Work Function and Corrosion Behaviors of Deformed Copper Surfaces,” Appl. Surf. Sci., 240(1–4), pp. 388–395. [CrossRef]
Meyers, M. , and Murr, L. , 1981, Shock Waves and High Strain Rate Phenomena in Metals, Plenum Press, New York.
Al Duheisat, S. , 2014, “ An Investigation of Mechanical Degradation of Pure Copper by Hydrogen,” Contemp. Eng. Sci., 7(4), pp. 165–178.
Zhang, W. , Yao, Y. L. , Engineering, M. , and York, N. , 2001, “ Microscale Laser Shock Processing—Modeling, Testing, and Microstructure Characterization,” J. Manuf. Process., 3(2), pp. 128–143. [CrossRef]
Meyers, M. A. , Jarmakani, H. , Bringa, E. M. , and Remington, B. A. , 2009, “ Dislocations in Shock Compression and Release,” Dislocations in Solids, J. P. Hirth, and L. Kubin , eds., Elsevier, Oxford, UK, pp. 91–197.
Nahme, H. , Worswick, M. , Nahme, H. , and Dynamic, M. W. , 1994, “ Dynamic Properties and Spall Plane Formation of Brass,” J. Phys. IV, 4(C8), pp. 707–712.
Duffy, T. S. , Ahrens, T. J. , and Samples, A. , 1997, “ Dynamic Compression of an Fe–Cr–Ni Alloy to 80 GPa,” J. Appl. Phys., 82(1997), pp. 4259–4269. [CrossRef]


Grahic Jump Location
Fig. 5

Hardness increases of AISI 4140 steel after cathodic charging. The level of LSP processing causes the hydrogen effects to be lessened, indicating mitigation to hydrogen embrittlement. The percent increases are lesser than for the stainless steel show.

Grahic Jump Location
Fig. 4

Hardness increases after cathodic charging on stainless steel samples, caused by increased hydrogen absorption into the lattice. The values on the abscissa correspond to the amount of overlapping between adjacent LSP pulses, and 2X indicates that the surface was treated with two passes. As the level of LSP processing increases, the amount of hardness changes via hydrogen decreases.

Grahic Jump Location
Fig. 3

Morphology of a patterned brass sample after LSP processing. Individual indentations are still visible because of the 0% overlap condition.

Grahic Jump Location
Fig. 2

Indentation profile of brass LSP processed at 250 mJ. More surface roughening effects are visible than on the stainless steel sample.

Grahic Jump Location
Fig. 1

LSP indentation profile of a stainless steel sample irradiated at 250 mJ with a spot size of 0.9 mm. The two lines are traces across perpendicular directions.

Grahic Jump Location
Fig. 6

SEM micrograph of the side of an untreated stainless steel U-bend specimens after 1 h of exposure to boiling magnesium chloride

Grahic Jump Location
Fig. 7

Untreated (a) and LSP treated (b) images showing the edge of stainless steel U-bend samples, where the bottom part of these images is the outer surface. LSP prevents cracks from propagating onto the outer surface in (b).

Grahic Jump Location
Fig. 8

Outer U-bent face for untreated stainless steel samples. Indicated by the arrow, cracking has occurred for the untreated sample, but was been prevented from occurring on the LSP treated sample.

Grahic Jump Location
Fig. 9

Optical micrographs of etched stainless steel samples exposed to 1 h of boiling magnesium chloride. (a) has not been LSP treated, and shows a combination of transgranular and intergranular fracture. (b) has been LSP treated, where the fracture mechanism is now dominated by intergranular fracture. The effects of increased hydrogen penetrating the lattice in (a) may cause the transgranular failure.

Grahic Jump Location
Fig. 10

Multiple cracks found in an AISI 4140 U-bend sample LSP three times at 300 mJ. Unlike the stainless steel, the high strength steel fails by many parallel cracks rather than one major failure.

Grahic Jump Location
Fig. 11

Mises stress in Pascals overlaid on the final deformed shape of a U-bend specimen from FEM simulation

Grahic Jump Location
Fig. 12

Tension on a path along the long direction in the center of the U-bend samples. The peak stress is higher for the brass.

Grahic Jump Location
Fig. 13

Work function measurements for brass, stainless steel, and high strength steel. The center of the LSP pulse is at 0 μm, and each material changes differently in response to the incident shockwave. Brass experiences work function decreases from LSP, while the high strength steel experiences an increased work function. The scale on the high strength steel figure covers a wider range than the other two, indicating an increased response to the shockwave processing.

Grahic Jump Location
Fig. 14

Rate of change of dislocation density, on the vertical axis for, varying amounts of plastic deformation. The three materials generate dislocations at varying rates. But since the yield strength of high strength steel is the largest, it will have lower dislocation generation for a given amount of deformation.

Grahic Jump Location
Fig. 15

Rate of change of dislocation density for high strength steel with three different types of heat treatments. As such, the downward slope of the annealed sample above 350 MPa does not indicate decreasing dislocation density but rather that dislocations are being generated at a slower rate.



Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In