Metal Oxycarbides as Cutting Tool Materials

[+] Author and Article Information
W. W. Carson, C. L. Leung, N. P. Suh

Department of Mechanical Engineering, Massachusetts Institute of Technology, Cambridge, Mass.

J. Eng. Ind 98(1), 279-286 (Feb 01, 1976) (8 pages) doi:10.1115/1.3438833 History: Received April 24, 1975; Online July 15, 2010

Abstract

The role of chemical stability of cutting tool materials in tool wear was investigated by studying the wear characteristics of titanium oxycarbides. The oxycarbides TiC0.25 O0.75 , TiC0.5 O0.5 , TiC0.6 O0.4 , and TiC0.75 O0.25 were produced by solid state interdiffusion of TiO and TiC. Their hardnesses and lattice spacings were determined as functions of their chemical composition. The chemical interaction of these oxycarbides with steel was investigated by diffusion couple experiments. Then commercially available cemented carbide tools were coated with TiC0.5 O0.5 and TiC0.75 O0.25 by RF diode sputtering. The wear resistance of these coated tools was determined by cutting tests. The wear rate of these oxycarbide coated tools was comparable to that of a TiC coated tool, although the free energies of formation of oxycarbides were lower and their hardnesses comparable. It is, therefore, concluded that while the data on free energy of formation and hardness can be useful in the initial screening steps of tool materials, the kinetics of the wear process needs to be more fully understood to define the chemical stability of tool materials in a cutting environment.

Copyright © 1976 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In